Refractory Insulation Rotary Kiln Bauxite for Castable Aggregate

• Customization: Available
• Refractoriness (℃): 1580< Refractoriness< 1770
• Shape: Block
• Model NO.: K-T
• Sample: Provide for Free
• Al2O3 Content: 65-90%
• Application: Refractory, Ceramics, Aluminum Industry.
• Bulk Density: 2.45 - 3.15
• K2o+Ca2o: <0.04%
• Color: Grey or Yellow
• Type: Refractory Material
• Material: Alumina Cement
• Transport Package: 25kg/PP Bag, or 1000kg/Jumbo Bag According to Cust
• Specification: 0-1mm, 1-3mm, 3-5mm, 5-8mm, 200mesh,
• Trademark: SWT-
• Origin: Henan. China
• HS Code: 250830000
• Production Capacity: 3000 T / Month

Product Description

         Refractory Insulation Rotary Kiln Bauxite for Castable Aggregate

Bauxite is one of the principal ore of aluminum.Bauxite contains hydrous aluminum oxides and aluminum hydroxides, formed through the laterization of aluminous rocks in tropical and subtropical areas .Bauxite is obtained by calcining (heating)superior grade bauxite at high temperature (from 850C to 1600C) .this can removes moisture thereby increasing the alumina content.

Classification Introduction:

1.Classified according to the type of bauxite raw materials:
   (1) raw bauxite, alumina original ore (natural sedimentary rock class).
   (2) the calcined bauxite, the raw bauxite after high temperature calcination (1200 ~ 1700 ºC)

2.Calssified according to the different calcining kiln where the bauxtie is divided into:
   (1)Shaft kiln bauxite
   (2)Rotary kiln bauxite
   (3)Round kiln bauxite

3.Calcined Bauxite according to different uses for division:
   (1) the refractory grade bauxite
   (2) the grinding grade alumina
   (3) the welding grade bauxite

Bauxite has a lot of different specifications like
Granular ( 0-1mm 1-3mm 3-5mm 5-8mm) 
Powder ( 200mesh 325mesh )
and big lump , the Al2O3 from 65-90%
we can also produce according to customers  special requirement 
 

Al2O3 content	Fe2O3 content	SiO2 content	TiO2(%)	bulk Density	Refractoriness
90%	1.5max	3.5max	3.8max	3.35min	1790ºC min
85%	2.0max	8.0max	4.0Max	3.2min	1790ºC min
80%	2.5max	10.0max	4.5Max	3.0min	1790ºC min
75%	3.0max	10.0max	5.0Max	2.9min	1770ºC min
70%	3.5max	10.0max	5.0Max	2.8min	1770ºC min
65%	4.0max	10.0max	5.0Max	2.7min	1770ºC min

Application of our calcined bauxite
Raw material for High Alumina brick;
Raw material for Refractory castable;
Raw material for Ramming mix;
Raw material for Nozzle;
Raw material for slide gate block;
Raw material for Refractory motar;